API 5CT Casing Pipe
Grade: H40, J55, K55, L80, L80-13Cr, L80-9Cr, N80-1, N80Q, P110
O.D: 4 1/2"-20"
Length: R1, R2, R3
Connection: STC, LTC, BTC, Premium Connection (VAM TOP, NEW VAM, PH-6)
Casing Pipe Data Table
| Labels a | OD mm |
Nominal Linear Mass b,c T&C kg/m |
WT t mm |
Type of end-finish d | ||||||||
| H40 | J55 K55 |
M65 | L80 R95 |
N80 Type 1, Q |
C90 T95 |
P110 | Q125 | |||||
| 1 | 2 | |||||||||||
| 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | 11 | 12 | 13 |
| 4-1/2 4-1/2 4-1/2 4-1/2 4-1/2 |
9.50 10.50 11.60 13.50 15.10 |
114.30 114.30 114.30 114.30 114.30 |
14.14 15.63 17.26 20.09 22.47 |
5.21 5.69 6.35 7.37 8.56 |
PS - - - - |
PS PSB PSLB - - |
PS PSB PLB PLB - |
- - PLB PLB - |
- - PLB PLB - |
- - PLB PLB - |
- - PLB PLB PLB |
- - - - PLB |
| 5 5 5 5 5 5 5 |
11.50 13.00 15.00 18.00 21.40 23.20 24.10 |
127.00 127.00 127.00 127.00 127.00 127.00 127.00 |
17.11 19.35 22.32 26.79 31.85 34.53 35.86 |
5.59 6.43 7.52 9.19 11.10 12.14 12.70 |
- - - - - - - |
PS PSLB PSLBE - - - - |
PS PSLB PLB PLB PLB - - |
- - PLB PLB PLB PLB PLB |
- - PLB PLB PLB PLB PLB |
- - PLB PLB PLB PLB PLB |
- - PLB PLB PLB PLB PLB |
- - - PLB PLB PLB PLB |
| 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 |
14.00 15.50 17.00 20.00 23.00 26.80 29.70 32.60 35.30 38.00 40.50 43.10 |
139.70 139.70 139.70 139.70 139.70 139.70 139.70 139.70 139.70 139.70 139.70 139.70 |
20.83 23.07 25.30 29.76 34.23 39.88 44.20 48.51 52.53 56.55 60.27 61.14 |
6.20 6.98 7.72 9.17 10.54 12.70 14.27 15.88 17.45 19.05 20.62 22.22 |
PS - - - - - - - - - - - |
PS PSLBE PSLBE - - - - - - - - - |
PS PSLB PLB PLB PLB - - - - - - - |
- - PLBE PLBE PLBE - - - - - - - |
- - PLBE PLBE PLBE - - - - - - - |
- - PLBE PLBE PLBE P P P P P P P |
- - PLBE PLBE PLBE - - - - - - - |
- - - - PLBE - - - - - - - |
| 6-5/8 6-5/8 6-5/8 6-5/8 |
20.00 24.00 28.00 32.00 |
168.28 168.28 168.28 168.28 |
29.76 35.72 41.67 47.62 |
7.32 8.94 10.59 12.06 |
PS - - - |
PSLB PSLBE - - |
PSLB PLB PLB - |
- PLBE PLBE PLBE |
- PLBE PLBE PLBE |
- PLBE PLBE PLBE |
- PLBE PLBE PLBE |
- - - PLBE |
| 7 7 7 7 7 7 7 |
17.00 20.00 23.00 26.00 29.00 32.00 35.00 |
177.80 177.80 177.80 177.80 177.80 177.80 177.80 |
25.30 29.76 34.23 38.69 43.16 47.62 52.09 |
5.87 6.91 8.05 9.19 10.36 11.51 12.65 |
PS PS - - - - - |
- PS PSLBE PSLBE - - - |
- PS PLB PLB PLB PLB - |
- - PLB PLB PLB PLB PLB |
- - PLB PLB PLB PLB PLB |
- - PLB PLB PLB PLB PLB |
- - - PLB PLB PLB PLBE |
- - - - - - PLB |
| 7 7 7 7 7 7 |
38.00 42.70 46.40 50.10 53.60 57.10 |
177.80 177.80 177.80 177.80 177.80 177.80 |
56.55 63.54 69.05 74.56 79.77 84.97 |
13.72 15.88 17.45 19.05 20.62 22.22 |
- - - - - - |
- - - - - - |
- - - - - - |
PLB - - - - - |
PLB - - - - - |
PLB P P P P P |
PLB - - - - - |
PLB - - - - - |
| 7-5/8 7-5/8 7-5/8 7-5/8 7-5/8 7-5/8 7-5/8 7-5/8 7-5/8 7-5/8 |
24.00 26.40 29.70 33.70 39.00 42.80 45.30 47.10 51.20 55.30 |
193.68 193.68 193.68 193.68 193.68 193.68 193.68 193.68 193.68 193.68 |
35.72 39.29 44.20 50.15 58.04 63.69 67.41 70.09 76.19 82.30 |
7.62 8.33 9.52 10.92 12.70 14.27 15.11 15.88 17.45 19.05 |
PS - - - - - - - - - |
- PSLB - - - - - - - - |
- PSLB PLB PLB - - - - - - |
- PLB PLB PLB PLB PLB PLB PLB - - |
- PLB PLB PLB PLB PLB PLB PLB - - |
- PLB PLB PLB PLB PLB PLB PLB P P |
- - PLB PLB PLB PLB PLB PLB - - |
- - - - PLB PLB PLB PLB - - |
| 7-3/4 | 46.10 | 196.85 | 68.60 | 15.11 | - | - | - | P | P | P | P | P |
| 8-5/8 8-5/8 8-5/8 8-5/8 8-5/8 8-5/8 8-5/8 |
24.00 28.00 32.00 36.00 40.00 44.00 49.00 |
219.08 219.08 219.08 219.08 219.08 219.08 219.08 |
35.72 41.67 47.62 53.57 59.53 65.48 72.92 |
6.71 7.72 8.94 10.16 11.43 12.70 14.15 |
- |
PS PS - PSLB PSLB PLB - |
PS PS PSLB PSLB PLB - - |
- - - PLB PLB PLB PLB |
- - - PLB PLB PLB PLBE |
- - - PLBE PLBE PLBE PLBE |
- - - PLB PLB PLB |
- - - - - PLB |
| 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 |
32.30 36.00 40.00 43.50 47.00 53.50 58.40 59.40 64.90 70.30 75.60 |
244.48 244.48 244.48 244.48 244.48 244.48 244.48 244.48 244.48 244.48 244.48 |
48.07 53.57 59.53 64.73 69.94 79.62 86.91 88.40 96.58 104.62 112.50 |
7.92 8.94 10.03 11.05 11.99 13.84 15.11 15.47 17.07 18.64 20.24 |
PS PS - - - - - - - - - |
- PSLB PSLB - - - - - |
- PSLB PSLB PLB PLB - - - - - |
- - PLB PLB PLB PLB PLB - - - - |
- - PLB PLB PLB PLB PLB - - - |
- - PLB PLB PLB PLB PLB P P P P |
- - - PLB PLB PLB PLB - - - - |
- - - - PLB PLB PLB - - - - |
| 10-3/4 10-3/4 10-3/4 10-3/4 10-3/4 10-3/4 10-3/4 10-3/4 10-3/4 10-3/4 |
32.75 40.50 45.50 51.00 55.50 60.70 65.70 73.20 79.20 85.30 |
273.05 273.05 273.05 273.05 273.05 273.05 273.05 273.05 273.05 273.05 |
48.74 60.27 67.71 75.90 82.59 90.33 97.77 108.93 117.86 126.94 |
7.09 8.89 10.16 11.43 12.57 13.84 15.11 17.07 18.64 20.24 |
PS PS - - - - - - - - |
- PSB PSB PSB - - - - - - |
- PSB PSB PSB PSB - - - - - |
- - - PSB PSB - - - - - |
- - - PSB PSB - - - - - |
- - - PSB PSB PSB PSB P P P |
- - - PSB PSB PSB PSB - - - |
- - - - - PSB PSB - - - |
| 11-3/4 11-3/4 11-3/4 11-3/4 11-3/4 11-3/4 |
42.00 47.00 54.00 60.00 65.00 71.00 |
298.45 298.45 298.45 298.45 298.45 298.45 |
62.50 69.94 80.36 89.29 96.73 105.66 |
8.46 9.53 11.05 12.42 13.56 14.78 |
PS - - - - - |
- PSB PSB PSB - - |
- PSB PSB PSB - - |
- - - PSB P P |
- - - PSB P P |
- - - PSB P P |
- - - PSB P P |
- - - PSB P P |
| 13-3/8 13-3/8 13-3/8 13-3/8 13-3/8 |
48.00 54.50 61.00 68.00 72.00 |
339.72 339.72 339.72 339.72 339.72 |
71.43 81.10 90.78 101.19 107.15 |
8.38 9.65 10.92 12.19 13.06 |
PS - - - - |
- PSB PSB PSB - |
- PSB PSB PSB - |
- - - PSB PSB |
- - - PSB PSB |
- - - PSB PSB |
- - - PSB PSB |
- - - - PSB |
| 16 16 16 16 |
65.00 75.00 84.00 109.00 |
406.40 406.40 406.40 406.40 |
96.73 111.61 125.01 162.21 |
9.53 11.13 12.57 16.66 |
PS - - - |
- PSB PSB P |
- PSB PSB - |
- - - P |
- - - P |
- - - - |
- - - P |
- - - P |
| 18-5/8 | 87.50 | 473.08 | 130.21 | 11.05 | PS | PSB | PSB | - | - | - | - | - |
| 20 20 20 |
94.00 106.50 133.00 |
508.00 508.00 508.00 |
139.89 158.49 197.93 |
11.13 12.70 16.13 |
PSL - - |
PSLB PSLB PSLB |
PSLB PSLB - |
- - - |
- - - |
- - - |
- - - |
- - - |
| P=Plain end; S=short round thread; L=Long round thread; B--Buttress thread; | ||||||||||||
|
a: Labels are for information and assistance in ordering. b: Nominal linear masses (col. 4) are shown for information only. c: The densities of martensitic chromium steels (L80 Types 9Cr and 13Cr) are different from carbon steels. The masses shown are therefore not accurate for martensitic chromium steels. A mass correction factor of 0.989 may be used. d: Buttress casing i s available with regualr, special clearance coupings or special clearance couplings with special bevel. |
||||||||||||
API 5CT MATERIALS CHEMICAL COMPOSITION
| Group | Grade | Type | C | Mn | Mo | Cr |
Ni max |
Cu max |
P max |
S max |
Si max |
||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| min | max | min | max | min | max | min | max | ||||||||
| 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | 11 | 12 | 13 | 14 | 15 | 16 |
|
1 |
H40 |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
– |
|
J55 |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
– |
|
|
K55 |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
– |
|
|
N80 |
1 |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
– |
|
|
N80 |
Q |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
– |
|
|
R95 |
– |
– |
0.45 c |
– |
1.9 |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
0.45 |
|
|
2 |
M65 |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
– |
|
L80 |
1 |
– |
0.43 a |
– |
1.9 |
– |
– |
– |
– |
0.25 |
0.35 |
0.03 |
0.03 |
0.45 |
|
|
L80 |
9Cr |
– |
0.15 |
0.3 |
0.6 |
0.9 |
1.1 |
8 |
10 |
0.5 |
0.25 |
0.02 |
0.01 |
1 |
|
|
L80 |
13Cr |
0.15 |
0.22 |
0.25 |
1 |
– |
– |
12 |
14 |
0.5 |
0.25 |
0.02 |
0.01 |
1 |
|
|
C90 |
1 |
– |
0.35 |
– |
1.2 |
0.25 b |
0.85 |
– |
1.5 |
0.99 |
– |
0.02 |
0.01 |
– |
|
|
T95 |
1 |
– |
0.35 |
– |
1.2 |
0.25 d |
0.85 |
0.4 |
1.5 |
0.99 |
– |
0.02 |
0.01 |
– |
|
|
C110 |
– |
– |
0.35 |
– |
1.2 |
0.25 |
1 |
0.4 |
1.5 |
0.99 |
– |
0.02 |
0.005 |
– |
|
|
3 |
P110 |
e |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.030 e |
0.030 e |
– |
|
4 |
Q125 |
1 |
– |
0.35 |
1.35 |
– |
0.85 |
– |
1.5 |
0.99 |
– |
0.02 |
0.01 |
– |
|
| a The carbon content for L80 may be increased up to 0.50 % maximum if the product is oil-quenched. b The molybdenum content for Grade C90 Type 1 has no minimum tolerance if the wall thickness is less than 17.78 mm. c The carbon content for R95 may be increased up to 0.55 % maximum if the product is oil-quenched. d The molybdenum content for T95 Type 1 may be decreased to 0.15 % minimum if the wall thickness is less than 17.78 mm. e For EW Grade P110, the phosphorus content shall be 0.020 % maximum and the sulfur content 0.010 % maximum. NL = no limit. Elements shown shall be reported in product analysis. |
|||||||||||||||
CASING PIPE MATERIALS – MECHANICAL PROPERTIES
| Group |
Grade |
Type |
Total elongation under load % |
Yield strength MPa |
Tensile strength min. MPa |
Hardness a max. |
Specified wall thickness mm |
Allowable hardness variation b HRC |
||
|---|---|---|---|---|---|---|---|---|---|---|
| min | max | HRC | HBW | |||||||
| 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | 11 |
| 1 |
H40 |
– |
0.5 |
276 |
552 |
414 |
– |
– |
– |
– |
|
J55 |
– |
0.5 |
379 |
552 |
517 |
– |
– |
– |
– |
|
|
K55 |
– |
0.5 |
379 |
552 |
655 |
– |
– |
– |
– |
|
|
N80 |
1 |
0.5 |
552 |
758 |
689 |
– |
– |
– |
– |
|
|
N80 |
Q |
0.5 |
552 |
758 |
689 |
– |
– |
– |
– |
|
|
R95 |
– |
0.5 |
655 |
758 |
724 |
– |
– |
– |
– |
|
| 2 |
M65 |
– |
0.5 |
448 |
586 |
586 |
22 |
235 |
– |
– |
|
L80 |
1 |
0.5 |
552 |
655 |
655 |
23 |
241 |
– |
– |
|
|
L80 |
9Cr |
0.5 |
552 |
655 |
655 |
23 |
241 |
– |
– |
|
|
L80 |
13Cr |
0.5 |
552 |
655 |
655 |
23 |
241 |
– |
– |
|
|
C90 |
1 |
0.5 |
621 |
724 |
689 |
25.4 |
255 |
≤ 12.70 12.71 to 19.04 19.05 to 25.39 ≥ 25.40 |
3.0 4.0 5.0 6.0 |
|
|
T95 |
1 |
0.5 |
655 |
758 |
724 |
25.4 |
255 |
≤ 12.70 12.71 to 19.04 19.05 to 25.39 ≥ 25.40 |
3.0 4.0 5.0 6.0 |
|
|
C110 |
– |
0.7 |
758 |
828 |
793 |
30 |
286 |
≤ 12.70 12.71 to 19.0 19.05 to 25.39 ≥ 25.40 |
3.0 4.0 5.0 6.0 |
|
| 3 |
P110 |
– |
0.6 |
758 |
965 |
862 |
– |
– |
– |
– |
| 4 |
Q125 |
1 |
0.65 |
862 |
1034 |
931 |
b |
– |
≤ 12.70 12.71 to 19.04 ≥ 19.05 |
3.0 4.0 5.0 |
| a In case of dispute, laboratory Rockwell C hardness testing shall be used as the referee method. b No hardness limits are specified, but the maximum variation is restricted as a manufacturing control in accordance with 7.8 and 7.9 of API Spec. 5CT. |
||||||||||