Products Description
| API 5CT K55 Casing Tubing Specifications | ||
| Available Sizes | 2 3/8″, 2 7/8″ and 3 ½" Outer Diameter | |
| Grades | J55, J55-FBNAU, N80, L80, P110 | |
| Tubing | 1 1/4 " – 2 1/16" Nom. | |
| Standards | API SPEC 5CT | |
| Model in Common Use | 2-3/8", 2-7/8", 3-1/2", 4", 4-1/2" | |
| Length Range | R1(6.10-7.32m), R2(8.53-9.75m), R3(11.58-12.8m) | |
| Steel Grade (Casing Grades, Tubing Grades) | J55, K55, N80-1, N80-Q, L80, P110 | |
| Type of Screw Thread | Non upset threaded end(NUE), External upset threaded end(EUE) | |
| Specialties |
Coating to customer specifications External upset Couplings – EUE, AB Modified, turned down, special clearance couplings Pup Joints Heat treating Hydrostatic Testing Drifting (Full-length, or just ends) Full third-party inspection capabilities (EMI, SEA, and Weld Line) Threading |
|
| End Finishing | External Upset Ends (EUE), Flush Joint, PH6 (and equivalent connections), Integral Joint (IJ) | |
API 5CT K55 Chemical Composition
| Group | Grade | Type | C | Mn | Mo | Cr | Ni max. | Cu max. | P max. | S max. | Si max. | ||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| min. | max. | min. | max. | min. | max. | min. | max. | ||||||||
| 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | 11 | 12 | 13 | 14 | 15 | 16 |
| 1 | H40 | - | - | - | - | - | - | - | - | - | - | - | 0.03 | 0.03 | - |
| J55 | - | - | - | - | - | - | - | - | - | - | - | 0.03 | 0.03 | - | |
| K55 | - | - | - | - | - | - | - | - | - | - | - | 0.03 | 0.03 | - | |
| N80 | 1 | - | - | - | - | - | - | - | - | - | - | 0.03 | 0.03 | - | |
| N80 | Q | - | - | - | - | - | - | - | - | - | - | 0.03 | 0.03 | - | |
| R95 | - | - | 0.45 c | - | 1.9 | - | - | - | - | - | - | 0.03 | 0.03 | 0.45 | |
| 2 | M65 | - | - | - | - | - | - | - | - | - | - | - | 0.03 | 0.03 | - |
| L80 | 1 | - | 0.43 a | - | 1.9 | - | - | - | - | 0.25 | 0.35 | 0.03 | 0.03 | 0.45 | |
| L80 | 9Cr | - | 0.15 | 0.3 | 0.6 | 0.9 | 1.1 | 8 | 10 | 0.5 | 0.25 | 0.02 | 0.01 | 1 | |
| L80 | 13Cr | 0.15 | 0.22 | 0.25 | 1 | - | - | 12 | 14 | 0.5 | 0.25 | 0.02 | 0.01 | 1 | |
| C90 | 1 | - | 0.35 | - | 1.2 | 0.25 b | 0.85 | - | 1.5 | 0.99 | - | 0.02 | 0.01 | - | |
| T95 | 1 | - | 0.35 | - | 1.2 | 0.25 d | 0.85 | 0.4 | 1.5 | 0.99 | - | 0.02 | 0.01 | - | |
| C110 | - | - | 0.35 | - | 1.2 | 0.25 | 1 | 0.4 | 1.5 | 0.99 | - | 0.02 | 0.005 | - | |
| 3 | P110 | e | - | - | - | - | - | - | - | - | - | - | 0.030 e | 0.030 e | - |
| 4 | Q125 | 1 | - | 0.35 | 1.35 | - | 0.85 | - | 1.5 | 0.99 | - | 0.02 | 0.01 | - | |
| a The carbon content for L80 may be increased up to 0.50 % maximum if the product is oil-quenched. b The molybdenum content for Grade C90 Type 1 has no minimum tolerance if the wall thickness is less than 17.78 mm. c The carbon content for R95 may be increased up to 0.55 % maximum if the product is oil-quenched. d The molybdenum content for T95 Type 1 may be decreased to 0.15 % minimum if the wall thickness is less than 17.78 mm. e For EW Grade P110, the phosphorus content shall be 0.020 % maximum and the sulfur content 0.010 % maximum. NL = no limit. Elements shown shall be reported in product analysis. |
|||||||||||||||
API 5CT k55 Gr. Mechanical Properties
| API 5CT Casing Standard | Type | API 5CT Casing Tensile Strength MPa |
API 5CT Casing Yield Strength MPa |
API 5CT Casing Hardness Max. |
|---|---|---|---|---|
| API SPEC 5CT | J55 | ≥517 | 379 ~ 552 | ---- |
| K55 | ≥517 | ≥655 | --- | |
| N80 | ≥689 | 552 ~ 758 | --- | |
| L80(13Cr) | ≥655 | 552 ~ 655 | ≤241HB | |
| P110 | ≥862 | 758 ~ 965 | ---- |
API 5CT K55 Tubing